Custom Vinyl Sheet Flooring Wood Look Supplier

Vinyl sheet flooring with a wood‑look surface combines a flexible PVC core with a printed decorative film that mimics natural grain. This construction delivers the visual warmth of hardwood while providing the moisture resistance and durability required in commercial settings.

Material Composition and Construction

The core is a calendered PVC sheet typically 2.0 mm to 3.0 mm thick, reinforced with a non‑woven fiberglass mat to limit linear expansion. Directly above the core, a transparent wear layer of urethane‑coated PVC provides abrasion resistance, and a high‑definition photographic film creates the wood visual.

Dimensional Stability and Wear Performance

Because the fiberglass reinforcement balances internal stresses, the product shows a dimensional change of less than 0.15 % after 24 hours at 70 °C and 90 % relative humidity, tested per ASTM F2199. The wear layer thickness ranges from 0.3 mm to 0.7 mm, offering a Taber abrasion resistance of ≤50 mg loss per 1000 cycles under CS‑17 wheels.

Customization Options

• Overall thickness: 2.0 mm – 3.5 mm (adjustable in 0.1 mm increments)
• Wear layer thickness: 0.3 mm – 0.7 mm
• Surface embossing: fine grain, medium grain, or synchronized emboss
• Edge treatment: straight, beveled, or cove‑able
• Color tone: light maple, walnut, gray‑washed, or custom RGB match

Performance Characteristics

Applications and Suitability

In healthcare facilities, the seamless sheet reduces crevices where pathogens can harbor, while the wear layer withstands frequent cleaning with disinfectants. Educational buildings benefit from the product’s low VOC emissions and impact resistance, which protects against dropped equipment in laboratories and workshops. Retail environments use the wood look to create a warm ambiance without the maintenance demands of real timber, and the flooring’s dimensional stability accommodates under‑floor heating systems common in modern office fit‑outs.

Quality Control and Testing

Each roll undergoes inline thickness gauging with laser sensors to maintain tolerance within ±0.05 mm. Wear layer adhesion is measured by peel strength testing, targeting a minimum of 2.5 N/mm. Visual inspection stations verify pattern registration and color consistency against a Pantone reference under D65 lighting. Final rolls are subject to a 24‑hour accelerated aging cycle to confirm long‑term dimensional stability before shipment.

Frequently Asked Questions

• Can dimensions be customized? – Yes, thickness, width, and length can be adjusted to project specifications.
• What information is required before quotation? – Required details include desired total area, thickness, wear layer, embossing preference, and any performance certifications needed.
• Which materials are available? – Base PVC with optional fiberglass reinforcement, urethane wear layer, and various PVC‑based decorative films.
• How is quality inspected? – Inline gauging, adhesion testing, visual checks, and accelerated aging as described above.
• What packaging methods are available? – Rolls are wrapped in polyethylene, placed on corrugated cores, and loaded onto pallets with edge protection.
• How are export shipments protected? – Pallets are strapped, covered with waterproof shrink film, and fitted with corner braces.
• What is the typical production lead time? – Lead time ranges from 10 to 20 working days depending on order complexity and current capacity.
• How are samples arranged? – Samples up to 1 m² can be shipped via express courier upon receipt of a formal request.

Next Steps

To obtain a detailed technical datasheet, discuss custom specifications, or request a quote, please contact our engineering team.